Paper Title :Microstructure, Microhardness and Tensile Properties of Al-Mn-0.5si Alloy Produced by Directional Solidification
Author :Hasan Kaya, Emin Cadirli, Ugur Buyuk
Article Citation :Hasan Kaya ,Emin Cadirli ,Ugur Buyuk ,
(2017 ) " Microstructure, Microhardness and Tensile Properties of Al-Mn-0.5si Alloy Produced by Directional Solidification " ,
International Journal of Mechanical and Production Engineering (IJMPE) ,
pp. 26-30,
Volume-5,Issue-9
Abstract : The directional solidification process of ternary Al-1.94Mn-0.5 Si eutectic alloy within a wide growth velocity
range from 8.3 to 978 μm/s was accomplished at a constant temperature gradient of 4.9 K/mm. The microstructures of
produced samples were characterized by using optical microscopy (OM), scanning electron microscopy (SEM) and Energy
dispersive x-ray analysis (EDX). Dendritic microstructures were observed in the directionally solidified samples. The
dendritic spacing tends to decrease with increasing growth velocity. As growth velocity increases, the dendritic spacing
decreased from 160 to 68 m. Microhardness and tensile strength at room temperature were examined by tensile tests. It
was found that the microhardness and ultimate tensile strength increased with increasing growth velocity, which ranged from
8.3 to 978 μm/s. Exponent values of the V for the microhardness and tensile strength were calculated as 0.05 and 0.09,
respectively. Fracture surface images of the studied alloys were analyzed depending on growth velocity. The fracture mode
transforms from ductile form to less ductile form with the increase of the growth velocity.
Index Terms— Fracture, microhardness, microstructure, tensile strength, Ternary eutectic alloy,
Type : Research paper
Published : Volume-5,Issue-9
DOIONLINE NO - IJMPE-IRAJ-DOIONLINE-9291
View Here
Copyright: © Institute of Research and Journals
|
|
| |
|
PDF |
| |
Viewed - 57 |
| |
Published on 2017-11-23 |
|