Paper Title :Mechanical Properties of Composites Materials Reinforced in Ceramic Particles
Author :Ruaa Haitham Abdul Raheem, Hiba Anwer Abdullah, Sura Salim Ahmed
Article Citation :Ruaa Haitham Abdul Raheem ,Hiba Anwer Abdullah ,Sura Salim Ahmed ,
(2017 ) " Mechanical Properties of Composites Materials Reinforced in Ceramic Particles " ,
International Journal of Mechanical and Production Engineering (IJMPE) ,
pp. 25-29,
Volume-5,Issue-6
Abstract : The complete dentures are made from different acrylic resins by various technologies. These materials are fragile
and frequently appear cracks that lead to fractures of prosthetic dentures. Many studies are done to develop the properties of
PMMA resin that is used for upper and lower complete denture base materials, by using composite materials consists of poly
methyl methacrylate (PMMA) resin as reference material, reinforcement with different weight fractions of ZrO2 particles (1%,
3%, 5%,7%) wt%. Acrylic resin (PMMA) and composite materials were prepared by Hand lay-up molding and investigated.
The investigated the mechanical properties were hardness, tensile properties (ultimate tensile strength (UTS), elongation at
break), impact properties (impact strength, fracture toughness), and flexural strength& shear stress. The resulting composites
of mechanical properties, composite materials with (Acrylic +7% ZrO2) has the maximum hardness of (72.4) shore D, The
ultimate tensile strength of 33.75MPa was obtained for (Acrylic +7% ZrO2), while the elongation at break decreases with
increase in filler concentration of 5 % was obtained for (Acrylic +7% ZrO2) is lower than other composites . The highest
impact strength with (Acrylic +3% ZrO2) (83 J/m2) than with other composites. The fracture toughness of the composites
increases with increase in the ZrO2 has the maximum value 1.998 MPa.m-1/2. Flexural strength & shear stress of the
composite materials increased with increasing of the weight fraction of ZrO2 particles at 7wt % (81)Mpa &(1.8)Mpa
respectively .
Index Terms- Acrylic resin, Zirconium Oxide, , mechanical properties.
Type : Research paper
Published : Volume-5,Issue-6
DOIONLINE NO - IJMPE-IRAJ-DOIONLINE-8469
View Here
Copyright: © Institute of Research and Journals
|
|
| |
|
PDF |
| |
Viewed - 66 |
| |
Published on 2017-08-30 |
|