Paper Title :Low Temperature Condition For Nio Nanoparticles Preparation Via Sol‐Gel Method
Author :P.V. Chai, Muneer. M. BA‐Abbad, Y.H. Teow, A.W. Mohammad
Article Citation :P.V. Chai ,Muneer. M. BA‐Abbad ,Y.H. Teow ,A.W. Mohammad ,
(2015 ) " Low Temperature Condition For Nio Nanoparticles Preparation Via Sol‐Gel Method " ,
International Journal of Advances in Science, Engineering and Technology(IJASEAT) ,
pp. 122-126,
Volume-3, Issue-3
Abstract : Nickel oxide (NiO) nanoparticles had been widely used in semiconductor, magnetic and fields due to its high
surface area, adsorptive and diffusivities properties. In this study, NiO was prepared via sol‐gel method under low
temperature operating condition. The properties of NiO nanoparticles were investigated by XRD, FTIR, TEM and TGA
analysis. TGA had confirmed the organic compound decomposed at 400oC and NiO nanoparticles were formed at this
temperature. The structure of NiO nanoparticles obtained was cubic structure. The spherical shape of NiO nanoparticles was
observed by TEM with average particle size of 18.11 nm which was close to the average particle size calculated using XRD
analysis of 22.78 nm. The sol‐gel method showed an easier way to produce smaller size of NiO nanoparticles at low
temperature.
Index Terms— Nickel Oxide, Nanoparticles, sol‐gel method, low temperature
Type : Research paper
Published : Volume-3, Issue-3
DOIONLINE NO - IJASEAT-IRAJ-DOIONLINE-2601
View Here
Copyright: © Institute of Research and Journals
|
|
| |
|
PDF |
| |
Viewed - 61 |
| |
Published on 2015-07-08 |
|